Composite coatings and methods therefor

ABSTRACT

An article includes a substrate and a coating provided on a surface of the substrate. The coating includes at least one metal silicide layer consisting essentially of MoSi 2  or WSi 2  or (Mo, W)Si 2  or a platinum group metal silicide and at least one layer consisting essentially of Si 3 N 4 .

BACKGROUND OF THE TECHNOLOGY

The present technology generally relates to coating systems and methods suitable for protecting articles or components exposed to high-temperature environments, such as the hostile thermal environment of a turbine engine. More particularly, the present technology relates to a coating that may serve as an oxidation resistant coating and/or as a bond coating to an environmental and/or thermal barrier coating.

Ceramic and refractory intermetallic materials and composites are currently being considered for such high temperature applications as combustor liners, vanes, shrouds, blades, and other hot section components of turbine engines, and for use in structures designed for service at high temperature in such applications as heat exchangers and internal combustion engines. Some examples of composite materials include silicon-containing composites, for example, composite materials in which silicon, silicon carbide (SiC), silicon nitride (Si₃N₄), and/or a refractory metal silicide serves as a reinforcement phase and/or a matrix phase. However, the environments characteristic of these applications often contain water vapor, which at high temperatures is known to cause significant surface recession and mass loss in silicon-bearing materials. The water vapor reacts with the structural material at high temperatures to form volatile silicon-containing species, often resulting in unacceptably high recession rates.

BRIEF DESCRIPTION OF THE TECHNOLOGY

The present technology provides composite coatings and methods of fabricating the composite coatings on an article or component formed of a silicon-containing material, such as a ceramic matrix composite (CMC). The composite coatings protect silicon-containing articles exposed to high temperatures, including the hostile thermal environment of a turbine engine.

According to one example of the technology, an article comprises a substrate and a coating provided on a surface of the substrate. The coating comprises at least one metal silicide layer consisting essentially of MoSi₂, WSi₂, or combinations of Mo and W silicide ((Mo, W)Si₂), or a platinum group metal silicide and at least one layer consisting essentially of Si₃N₄.

According to another example of the technology, an article comprises a substrate including a silicon-containing region that includes SiC, Si₃N₄, and/or a transition metal silicide as a reinforcement material in a metallic or a non-metallic matrix; and a coating provided on a surface of the substrate, the coating comprising MoSi₂ and Si₃N₄, wherein a percentage of Si₃N₄ is greater than about 55% by volume of the coating.

According to another example of the technology, a method of coating an article comprises applying a coating to a surface of the substrate, the coating comprising at least one metal silicide layer consisting essentially of MoSi₂ or WSi₂ or (Mo, W)Si₂ or a platinum group metal silicide and at least one layer consisting essentially of Si₃N₄.

According to another aspect of the technology, a method of coating an article comprising a substrate including a silicon-containing region that includes SiC, Si₃N₄, and/or a transition metal silicide as a reinforcement material in a metallic or a non-metallic matrix is provided, the method comprises applying a coating on a surface of the substrate, the coating comprising MoSi₂ and Si₃N₄, wherein a percentage of Si₃N₄ is greater than about 55% by volume of the coating.

BRIEF DESCRIPTION OF THE DRAWINGS

Other aspects and advantages of this technology will be better appreciated from the following detailed description with reference to the drawings, in which like reference numbers and characters refer to like features of the present technology, and wherein:

FIG. 1 schematically represents an article including a coating system according to one example of the present technology;

FIG. 2 schematically represents an article including a coating system according to another example of the present technology;

FIG. 3 schematically represents an article including a coating system according to another example of the present technology;

FIG. 4 schematically represents a method according to one example of the present technology;

FIG. 5 schematically represents a method according to another example of the present technology;

FIG. 6 schematically represents a method according to another example of the present technology;

FIG. 7 schematically represents a method according to another example of the present technology;

FIG. 8 schematically represents the relationship of multilayer expansion to a thickness ratio; and

FIG. 9 schematically represents the relationship of multilayer expansion to a volume fraction.

DETAILED DESCRIPTION OF THE TECHNOLOGY

The present technology is generally applicable to components or articles that operate within environments characterized by relatively high temperatures, severe thermal cycling and stresses, oxidation, and corrosion. Examples of such components include high and low pressure turbine vanes (nozzles) and blades (buckets), shrouds, combustor liners, augmentor hardware, and other hot section components of turbine engines, though the technology has application to other components.

Referring to FIG. 1, a component or article 10 includes a substrate 20 having a coating or coating system 30. The article 10 may also include an environmental barrier coating (EBC) and/or thermal barrier coating (TBC) 40 provided on the coating system 30. The EBC and/or TBC may be, for example, a multilayer coating system. The substrate 20 may include a silicon-containing region. Examples of silicon-containing materials include those with silicon, silicon carbide, silicon nitride, a silicide, for example, a transition metal silicide, wherein the transition metal is a refractory metal such as molybdenum or tungsten or combinations thereof, a platinum group metal such as platinum, iridium, or rhodium, for example in a matrix and/or reinforcement. Further examples include ceramic matrix composites (CMC) that contain silicon carbide as the reinforcement and matrix phases.

The coating system 30 may comprise two primary phases, molybdenum disilicide (MoSi₂) and silicon nitride (Si₃N₄). The coating system 30 may also comprise minor phases, for example Mo₅Si₃, Si, Mo₅Si₃C, SiC, and/or SiN_(x), for processing and/or property reasons. The minor phases may comprise less than 50% of the coating system 30. The percentage by volume of Si₃N₄ in the coating system may be greater than about 55%.

Referring to FIG. 2, a coating system 50 may include alternating layers 31, 33 of MoSi₂ and layers 32, 34 of Si₃N₄. It should be appreciated that although the initial layer 31 shown in FIG. 2 in contact with the substrate 20 is MoSi₂, the initial layer in contact with the substrate 20 may be Si₃N₄. It should also be appreciated that although two layers of MoSi₂ are shown alternating with two layers of Si₃N₄, the number of layers of MoSi₂ and Si₃N₄ may be any number, including a single layer of each. It should be further appreciated that although the number of layers of MoSi₂ and Si₃N₄ are shown as equal, the number of layers of each may be unequal. For example, the coating system may include four layers of MoSi₂ and three layers of Si₃N₄, or vice versa.

Referring to FIG. 3, a coating system 60 may include alternating layers 31, 33 of MoSi₂ and layers 32, 34 of Si₃N₄. Transition regions 35 may be provided between the alternating layers 31, 32; 32, 33; 33, 34. The transition regions 35 include a mixture of both phases of MoSi₂ and Si₃N₄. The transition regions 35 may also include minor phases as described above. The transition regions 35 may be formed as described in more detail below. As discussed above with respect to FIG. 2, although the coating system 60 is shown in FIG. 3 as including a first layer 31 of MoSi₂ in contact with the substrate 20 and an equal number of layers of MoSi₂ and Si₃N₄, it should be appreciated that the coating system 60 may be as described above with respect to the variations of FIG. 2.

Referring to FIGS. 4-7, various methods for coating an article or component including a substrate are schematically illustrated. As like reference numbers refer to like features of the example methods, those features that are common to two or more of the example methods will only be described with reference to one example method.

Referring to FIG. 4, a method of coating an article starts at S100. In S120 MoSi₂ is deposited on the surface of the substrate to form a layer of MoSi₂ on the substrate.

After formation of the layer of MoSi₂, a Si₃N₄ layer is formed on the MoSi₂ layer in S150. If the combined thickness t of the MoSi₂ layer and the Si₃N₄ layer is less than a predetermined thickness t_(p) (S170: Yes), the process returns to S120 for formation of an additional layer of MoSi₂. When the combined thickness t of the MoSi₂ layer and the Si₃N₄ layer is not less than the predetermined thickness t_(p) (S170: No), the process ends at S180.

Referring to FIG. 5, according to another example, a method of coating an article starts in S100. In S142, after formation of the MoSi₂ layer, a transition region of MoSi₂ and Si₃N₄ is formed. The mixture of both phases provides transition regions between the layers of MoSi₂ and Si₃N₄, for example as described above with reference to FIG. 3.

Referring to FIG. 6, in S172, the alternating MoSi₂ and Si₃N₄ layers are heat treated to form a dual-phase mixture of MoSi₂ and Si₃N₄. It should be appreciated that a heat treatment step may also be included in the method illustrated in FIG. 5

Referring to FIG. 7, according to another example, in S112 a dual-phase mixture of MoSi₂ and Si₃N₄ may be formed having a predetermined volume ratio. The process parameters and/or conditions may be determined to achieve a dual-phase mixture of MoSi₂ and Si₃N₄ with a volume ratio that reduces, or minimizes, a CTE mismatch to the substrate. The process parameters and/or conditions may be determined to control the species and/or volume fraction of the minor phases. The process conditions and/or parameters may be adjusted during the coating process to achieve a coating with a graded microstructure and properties across its thickness.

It should be appreciated that the coatings described herein may be formed by various processes, including for example CVD, ion plasma deposition, and physical vapor deposition (e.g. evaporation or sputtering).

It should further be appreciated that the mechanism of reducing the CTE mismatch between the coating and the substrate operates differently between the examples of layer-by-layer coatings (e.g. FIGS. 2 and 3) and the examples of a layer including a mixture of the phases of MoSi₂ and Si₃N₄. In the case of the layer-by-layer coatings, the desired ratio of MoSi₂ to Si₃N₄ thicknesses may be determined from an effective coefficient of thermal expansion α_(eff). For a multilayer coating of MoSi₂ and Si₃N₄ layers, the effective coefficient of thermal expansion may be calculated using a linear elastic analysis according to the following equation:

α_(eff)=(t _(MoSi2)E′_(MoSi2)α_(MoSi2) +t _(Si3N4)E′_(Si3N4)α_(Si3N4))/(t _(MoSi2)E′_(MoSi2) +t _(Si3N4)E′_(Si3N4))

where for each material i, t_(i) is the sum thickness of all layers in the stack, E′_(i) is the biaxial elastic modulus, defined as E′_(i)=E_(i)/(1−ν_(i)), ν_(i) is the Poisson's ratio, and α_(i) is the thermal expansion coefficient. Rearranging, the ratio of thicknesses is related to the effective thermal expansion by:

t _(MoSi2) /t _(Si3N4)=−((α_(eff)−α_(Si3N4))/(α_(eff)−α_(MoSi2)))(E′_(Si3N4)/E′_(MoSi2)).

Taking representative values for the materials of interest:

Si₃N₄: α_(Si3N4)=3.3×10⁻⁶/C; E_(Si3N4)=310 GPa; ν_(Si3N4)=0.25→>E′_(Si3N4)=413 GPa; MoSi₂: α_(MoSi2)=8.25×10⁻⁶/C; E_(MoSi2)=432 GPA; ν_(MoSi2)=0.16→E_(MoSi2)=514 GPa.

The relationship between the multilayer expansion and the thickness ratio is illustrated in FIG. 8 and the relationship between the multilayer expansion and volume fraction is illustrated in FIG. 9.

In considering examples of, for example, a substrate having a SiC matrix and SiC reinforcement, to match the CTE of SiC (α_(eff)=α_(SiC)˜4.5×10⁻⁶/C), t_(MoSi2)/t_(Si3N4)˜0.26. To match the CTE of SiC+25% (α_(eff)=1.25α_(SiC)˜6.9×10⁻⁶/C), t_(MoSi2)/t_(Si3N4)˜0.71. To match the CTE of SiC−25% (α_(eff)=0.75α_(SiC)˜3.4×10⁻⁶/C), t_(MoSi2)/t_(Si3N4)˜0.01.

A MoSi₂:Si₃N₄ thickness ratio may thus be, for example, about 0.01 to about 0.75, or for example about 0.01 to about 0.45. The corresponding MoSi₂ volume fractions (V_(MoSi2)), calculated as V_(MoSi2)=t_(MoSi2)/(t_(Si3N4)+t_(MoSi2)), may thus be, for example about 1 to about 45 vol % MoSi₂, or for example about 10 to about 30 vol % MoSi₂.

It should be appreciated that WSi₂ or (Mo, W)Si₂ or Platinum (Pt) group silicides may be used in place of MoSi₂ in the examples discussed above.

When a MoSi₂ or WSi₂ or a (Mo, W)Si₂/Si₃N₄ mixture is oxidized in an oxygen-bearing atmosphere such as air, the Si is preferentially oxidized while the Mo and/or W is rejected into the coating. If the coating is thick with respect to the SiO₂ layer formed by oxidation, the silicide or silicide/Si₃N₄ mixture is largely preserved in the substrate beneath the oxide, and the excess Mo and/or W rejected into the bulk of the coating forms Mo₅Si₃ and/or W₅Si₃ particles.

On the other hand, if the silicide is a Pt group silicide interlayered with Si₃N₄, the Pt group metal will be left behind when all of the Si in the silicide layer has been consumed because condensed-phase oxides of the Pt group metals are not stable at temperatures above 1400° C. The final state of the silicide layer is likely to be an amorphous SiO₂ layer with second phase Pt group metal particles. Oxidation will then pass on into the Si₃N₄ layer below the silicide layer, and so on, with few or no negative consequences.

While the technology has been described in terms of the disclosed examples, it should be appreciated that other forms could be adopted by one skilled in the art. Therefore, the scope of the inventions is to be defined only by the following claims. 

1. An article, comprising: a substrate; and a coating provided on a surface of the substrate, the coating comprising at least one metal silicide layer consisting essentially of MoSi₂ or WSi₂ or (Mo, W)Si₂ or a platinum group metal silicide; and at least one layer consisting essentially of Si₃N₄.
 2. The article according to claim 1, wherein the at least one metal silicide layer is in contact with the surface of the substrate.
 3. The article according to claim 1, wherein the at least one layer of Si₃N₄ is in contact with the surface of the substrate.
 4. The article according to claim 1, further comprising: at least one transition region between the at least one metal silicide layer and the at least one layer of Si₃N₄, the transition region including a mixture of both the metal silicide layer and Si₃N₄.
 5. The article according to claim 1, further comprising: a plurality of metal silicide layers consisting essentially of MoSi₂ or WSi₂ or (Mo, W)Si₂ or a platinum group metal silicide; and a plurality of layers consisting essentially of Si₃N₄, wherein the layers of metal silicide and Si₃N₄ are alternating.
 6. The article according to claim 1, wherein a thickness ratio of the at least one metal silicide layer and the at least one layer of Si₃N₄ provides the coating with a coefficient of thermal expansion substantially equal to a coefficient of thermal expansion of the substrate.
 7. The article according to claim 1, wherein the substrate includes SiC, Si₃N₄, a transition metal silicide, and/or silicon as a reinforcement or matrix phase.
 8. The article according to claim 1, further comprising: at least one of an environmental barrier coating and a thermal barrier coating provided on the coating.
 9. The article according to claim 1, wherein a percentage of Si₃N₄ is greater than about 55% by volume of the coating.
 10. The article according to claim 1, wherein the at least one metal silicide layer consists essentially of MoSi₂ that is about 1% to about 45% of the volume of the coating.
 11. The article according to claim 1, wherein the least one metal silicide layer consists essentially of MoSi₂ and a ratio of the thickness of the at least one layer of MoSi₂ to the thickness of the at least one layer of Si₃N₄ is about 0.01 to about 0.75.
 12. An article, comprising: a substrate including a silicon-containing region that includes SiC, Si₃N₄, a transition metal silicide, and/or silicon as a reinforcement material in a metallic or a non-metallic matrix; and a coating provided on a surface of the substrate, the coating comprising MoSi₂ and Si₃N₄, wherein a percentage of Si₃N₄ is greater than about 55% by volume of the coating.
 13. The article according to claim 12, wherein the MoSi₂ and Si₃N₄ are in a mixture.
 14. The article according to claim 13, wherein the mixture is functionally graded.
 15. The article according to claim 13, wherein the mixture further comprises: Mo₅Si₃, Si, and/or SiN_(x).
 16. A method of coating an article comprising a substrate, the method comprising: applying a coating to a surface of the substrate, the coating comprising at least one metal silicide layer consisting essentially of MoSi₂ or WSi₂ or (Mo, W)Si₂ or a platinum group metal silicide and at least one layer consisting essentially of Si₃N₄.
 17. The method according to claim 16, wherein the at least one metal silicide layer is in contact with the surface of the substrate.
 18. The method according to claim 16, wherein the at least one layer of Si₃N₄ is in contact with the surface of the substrate.
 19. The method according to claim 14, wherein the at least one metal silicide layer and the at least one layer of Si₃N₄ are applied by chemical vapor deposition.
 20. The method according to claim 16, further comprising: forming a transition region between the at least one metal silicide layer and the at least one layer of Si₃N₄, the transition region including a mixture of both phases of the metal silicide and Si₃N₄.
 21. The method according to claim 16, further comprising: forming a plurality of metal silicide layers consisting essentially of MoSi₂ or WSi₂ or (Mo, W)Si₂ or a platinum group metal silicide and forming a plurality of layers consisting essentially of Si₃N₄, wherein the metal silicide layers and Si₃N₄ are alternating.
 22. The method according to claim 16, wherein a thickness ratio of the at least one metal silicide layer and the at least one layer of Si₃N₄ provides the coating with a coefficient of thermal expansion substantially equal to a coefficient of thermal expansion of the substrate.
 23. The method according to claim 16, wherein the substrate includes SiC, Si₃N₄, a transition metal silicide, and/or silicon as a reinforcement or matrix phase.
 24. The method according to claim 16, further comprising: applying at least one of an environmental barrier coating and a thermal barrier coating on the coating.
 25. The method according to claim 16, wherein a percentage of Si₃N₄ is greater than about 55% by volume of the coating.
 26. The method according to claim 16, further comprising: heat treating the coating to form a mixture of metal silicide and Si₃N₄.
 27. A method of coating an article comprising a substrate including a silicon-containing region that includes SiC, Si₃N₄, a transition metal silicide, and/or silicon as a reinforcement material in a metallic or a non-metallic matrix, the method comprising: applying a coating on a surface of the substrate, the coating comprising MoSi₂ and Si₃N₄, wherein a percentage of Si₃N₄ is greater than about 55% by volume of the coating.
 28. The method according to claim 27, wherein the MoSi₂ and Si₃N₄ are in a mixture.
 29. The method according to claim 28, wherein the mixture is functionally graded.
 30. The method according to claim 28, wherein the mixture further comprises: Mo₅Si₃, Si, and/or SiN_(x). 